Grades for Applications and Materials - ISO P
|
Application
|
Grades
|
|
|
|
|
|
|
ISO
P05-P15
|
|
Coating Layers
|
|
Recommended Application
A hard substrate, MTCVD TiCN and thick Al2O3 coated grade with post coating surface treatment. Mainly used for turning nodular cast iron (may be used for other cast iron as well) at medium to high cutting speeds at stable or slightly unstable conditions. May be used when higher wear resistance than that provided by IC5010 or other grades is required.
|
|
Harder
Tougher
|
|
IC5005
|
|
IC9150
|
|
IC8150
|
IC8250 | IC9250 |
|
|
|
Application
|
Grades
|
|
|
|
|
|
|
ISO
P01-P30
|
|
Coating Layers
|
|
Recommended Application
A very hard substrate with a cobalt enriched layer, MTCVD TiCN and a thick α Al2O3 CVD coating. Features excellent thermal stability and resistance to chipping and plastic deformation. Recommended for high speed machining of steel at stable or slightly unstable conditions
|
|
Harder
Tougher
|
|
IC5005
|
|
IC9150
|
|
TP20
|
IC8150 | IC8250 | IC9250 |
|
IC8005
|
|
|
|
Application
|
Grades
|
|
ISO P
|
|
|
1-11
|
12-13
|
|
|
Steel
|
Stainless Steel Ferritic & Martensitic
|
|
|
|
|
|
|
ISO
P10-P30
|
|
Coating Layers
|
|
Recommended Application
A very hard substrate with a cobalt enriched outer layer, MTCVD TiCN and a thick α Al2O3 CVD coating with post coating surface treatment. Features excellent thermal stability and resistance to chipping and plastic deformation. Recommended for high speed machining of steel at stable or slightly unstable conditions and nodular cast iron at interrupted cut conditions. IC8150 can be used for machining stainless steel at low to medium feed and high cutting speed.
|
|
Harder
Tougher
|
|
|
|
IC8150(9150)
|
|
IC8250(9250)
|
| IC8350(9350) | IC807(907) | |
|
IC3028
|
|
|
IC807(907)
|
|
|
|
IC908(808)
|
IC6015 | | IC6025 | IC830(3028) |
|
IC3028
|
|
|
Coolant
|
Y
|
N
|
|
|
Application
|
Grades
|
|
ISO P
|
|
|
1-11
|
12-13
|
|
|
Steel
|
Stainless Steel Ferritic & Martensitic
|
|
|
|
|
|
|
ISO
P10-P35
|
|
Coating Layers
|
|
Recommended Application
A tough substrate with a cobalt enriched outer layer combined with MTCVD TiCN and a thick alpha Al2O3 CVD coating with post coating surface treatment. IC8250 features excellent thermal stability and resistance to plastic deformation. Recommended for general machining of alloyed and stainless steel in a wide range of conditions, featuring high toughness and wear resistance
|
|
Harder
Tougher
|
|
|
|
IC8150(9150)
|
|
IC8250(9250)
|
| IC8350(9350) | IC807(907) | |
|
IC3028
|
|
|
IC807(907)
|
|
|
|
IC908(808)
|
IC6015 | | IC6025 | IC830(3028) |
|
IC3028
|
|
|
Coolant
|
Y
|
N
|
|
For more information contact: Industrealize@iscar.co.il